IP Annals of Prosthodontics and Restorative Dentistry (APRD) open access, peer-reviewed quarterly journal publishing since 2015 and is published under the Khyati Education and Research Foundation (KERF), is registered as a non-profit society (under the society registration act, 1860), Government of India with the vision of various accredited vocational courses in healthcare, education, paramedical, yoga, publication, teaching and research activity, with the aim of faster and better dissemination of knowledge, we will be publishing the article more...Original Article
Author Details :
Volume : 9, Issue : 3, Year : 2023
Article Page : 158-164
https://doi.org/10.18231/j.aprd.2023.031
Abstract
Background: Co-Cr alloys are most commonly used base metal alloy in dentistry for the fabrication of many types of metallic substructures. They gained popularity due to their good mechanical properties and low cost. There are different techniques for fabrication of Co-Cr alloys which includes casting and DMLS technique. However, change in the fabrication techniques showed variation in mechanical properties.
Materials and Methods: Forty Co-Cr samples each were made from two different techniques, Casting and DMLS. Fracture toughness was done with charpy’s impact test machine and fatigue behaviour test was done with nano universal testing machine. The samples were later observed under stereo electron microscope to assess the kind of failure.
Results: Unpaired t test revealed that there was statistically significant difference between two different groups. The mean difference of fracture toughness in Casting group was higher when compared with DMLS group. The number of fatigue cycles were higher in DMLS group than the casting group.
Conclusion: Within the limitations of this in vitro study, casting group showed higher fracture toughness when compared to DMLS group, whereas fatigue limit was higher in DMLS group than casting group.
Keywords: Fatigue Behaviour, Fracture Toughness of Cobalt Chromium, Alloy Fabricated
How to cite : Harika C, Reddy K M, Adithya V, Comparison of fatigue behaviour and fracture toughness of cobalt chromium alloy fabricated by casting and selective laser melting methods. IP Ann Prosthodont Restor Dent 2023;9(3):158-164
This is an Open Access (OA) journal, and articles are distributed under the terms of the Creative Commons Attribution-NonCommercial-ShareAlike 4.0 License, which allows others to remix, tweak, and build upon the work non-commercially, as long as appropriate credit is given and the new creations are licensed under the identical terms.